A novel surface strengthening technique for enhancing fatigue properties of 6061 Al alloy

Gong B., Zhang Z., Wang H., Liu R., Liu H., Wang H., ...Daha Fazla

International Journal of Fatigue, cilt.198, 2025 (SCI-Expanded) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 198
  • Basım Tarihi: 2025
  • Doi Numarası: 10.1016/j.ijfatigue.2025.109000
  • Dergi Adı: International Journal of Fatigue
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, PASCAL, Aerospace Database, Communication Abstracts, Compendex, INSPEC, Metadex, zbMATH, Civil Engineering Abstracts
  • Anahtar Kelimeler: 6061 Al alloy, Fatigue strength, Hardness, Residual stress, Spinning rolling, Surface roughness
  • Recep Tayyip Erdoğan Üniversitesi Adresli: Evet

Özet

A new surface spinning rolling (SR) strengthening technique was developed to enhance the fatigue properties of 6061 Al alloy. The traditional shot peening (SP) process can strengthen the sample's surface, but it increases surface damage, which seriously hinders the improvement of fatigue performance. However, the SR process not only introduces a high residual compressive stress and a hardened layer on the sample surface but also remarkably lowers the surface roughness. Moreover, the SR treatment formed a gradient microstructure on the surface layer of 6061 Al alloy, effectively postponing the initiation and propagation of fatigue cracks. Fatigue experiments demonstrate that after SR treatment, the fatigue strength of 6061 Al alloy increases by 17.9 %, from 223 MPa to 263 MPa. This study demonstrates the significant advantages by the SR process in producing high fatigue-resistant Al alloy components.